​ ​​CA COMPOSITES Limited

  • Epoxy Resin for Vacuum Infusion

Model: CAMG-4626
Tg: 105-115 ℃
Viscosity at 25℃ : Black thick paste
Curing condition: 6-8 hours at 50℃(initial cure)+ 5 hours at 100 ℃

  • Tooling Epoxy Gel coat

Room Temperature Curing Low Tg Infusion epoxy resin

Model: CALT-5028
Tg: 75-85 ℃
Viscosity at 25℃ : 200-300 cps
Flexure Strength: 100-125 MPa
Curing condition: 24 hours at RT(25℃)+ 6 hours at 70℃(post cure) or 

                                    4 hours at  50 ℃(initial cure) +  6 hours at 70℃ (post cure)

  • Epoxy resin for Hand Lay-up process

Epoxy Resin

We supply high quality epoxy resins applicable in making  composite parts as well as tooling/mould.

These can be used along with carbon/glass/Kevlar fibers , PVC foam cores and honeycomb cores.

At present, we supply the following types of epoxy resins

Medium Tg Infusion Epoxy resin

Model: CAML-5417
Tg: 115-125 ℃
Viscosity at 25℃ : 200-300 cps
Flexure Strength: 100-125 MPa
Curing condition: 6-8 hours at 50℃(initial cure)+ 5 hours at 100 ℃

​Applicable for making moulds

Medium Tg Hand lay up Epoxy resin

Model: CAML-5115
Tg: 100-115 ℃
Viscosity at 25℃ : 200-300 cps
Flexure Strength: 100-130 MPa
Curing condition: 5 hours at 50℃(initial cure)+ 5 hours at 100 ℃

Applicable in making moulds


Room temperature Curing Hand lay up Epoxy Resin

Model: CALT-5089
Tg: 75-85 ℃
Viscosity at 25℃ : 800-2000 cps
Flexure Strength: 100-125 MPa
Curing condition: 24 hours at 25℃ (initial cure) + 6 hours at 70℃ or

                        4 hours at  50 ℃(initial cure) +  6 hours at 70℃ (post cure)

Options on Hardener

Fast : 30-60 minutes Pot life
Slow: 100-120 minutes Pot life


We can ship these products to every countries by air or water.